A device and a method for solvent vapor smoothing of a surface of a plastic product

ABSTRACT

The disclosure relates to smoothing of a surface of models made by additive manufacturing process utilizing melted polymer layers, by condensation of solvent vapors thereon. A method for solvent vapor smoothing of a surface of a plastic product by: placing the plastic product to be smoothed in a closed chamber (110) having heated walls (112-116) and a heated evaporator (111) for solvent; determining process parameters; heating (503) at least one wall (112-116) of the chamber (110) to a first temperature and heating the evaporator (111) to a second temperature; introducing (504) a solvent to the evaporator (111); allowing (506) the solvent vapors to condense on the outer surface of the product; and collecting solvent vapors from the chamber (110).

TECHNICAL FIELD

The present disclosure relates to a device and a method for solventvapor smoothing of a surface of a plastic product. In particular, thepresent disclosure relates to smoothing of a surface of models made byadditive manufacturing process utilizing melted polymer layers, bycondensation of solvent vapors thereon.

BACKGROUND

Products made by increasingly popular 3D printing technologies usuallyhave a layered structure, which is visible by a naked eye. This relatesin particular to Layer Plastic Deposition (LPD) technology, wherein athermoplastic material (filament) is melted in an extruder and layeredon a working platform, thereby creating a three-dimensional product.

In order to enhance visual aspects of such products, their surface maybe smoothed by means of a process known as solvent vapor smoothing, inwhich the product is treated with a solvent vapor which condenses on asurface of the product, thereby making it smoother.

There are known various devices for performing the solvent vaporsmoothing process, typically comprising a chamber in which a treatedobject is placed to be in contact with solvent vapors.

The process of solvent vapor smoothing of plastic products performed bythe known devices and methods is typically a long lasting process inwhich highly concentrated solvents are used. This causes severalproblems. For example, it is difficult to avoid emission of harmfulsolvent vapors from the working chamber of the device to the ambientenvironment. Moreover, the smoothing process is not uniform and in someregions the product subject to the smoothing process tends to deform,while in other regions the surface is not smoothed to a satisfactorydegree.

Therefore, there is a need to provide an improved device and a methodfor solvent vapor smoothing of a surface of a plastic product.

SUMMARY

There is disclosed a method for solvent vapor smoothing of a surface ofa plastic product, the method comprising the steps of: placing theplastic product to be smoothed in a closed chamber comprising heatedwalls and a heated evaporator for solvent; determining processparameters, comprising an expected dew point of the solvent and anexpected boiling temperature of the solvent; heating at least one wallof the chamber to a first temperature and heating the evaporator to asecond temperature, wherein the first temperature is higher than theexpected dew point temperature of the solvent and wherein the secondtemperature is higher than the expected boiling temperature of thesolvent for a current pressure within the chamber; introducing a solventto the evaporator; allowing the solvent vapors to condense on the outersurface of the product; and collecting solvent vapors from the chamber.

The evaporator for solvent may be located at a bottom of the chamber;and the method further comprises circulating solvent vapors inside thechamber in a direction from the bottom to a top of the chamber; andcollecting solvent vapors from the upper portion of the chamber.

The chamber may have heated walls and the method further comprises,after allowing the solvent vapors to condense on the outer surface ofthe product, heating at least one wall of the chamber, collectingsolvent vapors from the chamber and condensing the collected solventvapors outside the chamber.

The method may further comprise, before introducing the solvent to theevaporator, generating within the chamber a negative pressure withrespect to an ambient pressure.

The negative pressure may equal 300 to 800 mbar.

There is further disclosed a device for solvent vapor smoothing of asurface of a plastic product, the device comprising: a closed chambercomprising heated walls and a heated evaporator for solvent; acontroller configured to, before introducing the solvent to theevaporator: determine process parameters, comprising an expected dewpoint of the solvent and an expected boiling temperature of the solvent;and activate heating elements to heat at least one wall of the chamberto a first temperature and heat the evaporator to a second temperature,wherein the first temperature is higher than the expected dew pointtemperature of the solvent and wherein the second temperature is higherthan the expected boiling temperature of the solvent for a currentpressure within the chamber.

The evaporator for solvent may be located at a bottom of the chamber;and the device may further comprise a circulation system for circulatingsolvent vapors inside the chamber in a direction from the bottom to atop of the chamber and outside the chamber in a direction from the topto the bottom of the chamber in a closed loop system.

The chamber may further comprise a refrigerating module for collectingsolvent vapors from the chamber; and the controller is furtherconfigured to, after allowing the solvent vapors to be condensed on theouter surface of the product: activate the heating elements to heat atleast one wall of the chamber; and activate the refrigerating module tocondense the collected solvent vapors outside the chamber.

The device may further comprise a pressure module with a vacuum pump forproducing a negative pressure within the chamber.

The refrigerating module may comprise air ducts for guiding thecollected solvent vapors, wherein the air ducts are thermally coupledwith Peltier modules.

The warm side of the Peltier modules may be coupled with a heat sinkcooled by a cooling fan.

The device may further comprise a strain gauge mounted on an outersurface of a side wall of the chamber.

The device may further comprise an electromagnetic lock for securing thedoor of the chamber during the smoothing process.

The device may further comprise a transfer tube for guiding solventvapors from an inlet at the upper portion of the chamber to a mainsolvent tank under the force of gravity.

The solvent may be transferrable from the main solvent tank to theevaporator under the force of gravity via a solvent dosing valve.

The method and device as defined above are particularly useful forimproving the solvent vapor smoothing process with respect to theproblem of preventing condensation of solvent on walls to improve thesolvent concentration within the chamber and/or to avoid solventdropping from the top wall towards the heated object, by generating ahigh temperature gradient between the product and solvent vapors beforestarting the vaporization.

The other, optional features of the method and device are useful forimproving the solvent vapor smoothing process with respect to variousother problems, such as, but not limited to:

-   -   the tendency of the small elements (details) of the product to        bend downwards under gravity due to the melting action of the        solvent and the high temperature, by circulating solvent vapors        inside the chamber in a direction from the bottom to a top of        the chamber;    -   efficiently removing the solvent vapors from the chamber and the        product by cooling and condensing the solvent vapors at the end        of the process;    -   preventing the chamber from depressurization (leaking) due to        subsequent increase of pressure during solvent vaporization, by        generating a negative pressure within the chamber.

BRIEF DESCRIPTION OF DRAWINGS

The device and the method presented herein are presented by means ofexample embodiments on a drawing, wherein:

FIG. 1a presents a device for solvent vapor smoothing in an isometricview;

FIG. 1b presents the device with a cut-out view of a circulation system;

FIG. 2 presents the device without a cover in an isometric view;

FIG. 3 presents the device without the cover in a back view;

FIG. 4 presents the device without the cover and without a refrigeratingsystem in an isometric view;

FIG. 5 presents the device without the cover and without a heat sink inan isometric view;

FIG. 6 presents details of a sleeve and a driving shaft in an explodedview;

FIG. 7 presents steps of a solvent vapor smoothing process.

DETAILED DESCRIPTION

FIG. 1a presents an example embodiment of a device for solvent vaporsmoothing in an isometric view. The device comprises a chamber 110closed by a sealed door 120. Preferably, the chamber 110 is made ofmetal. A product to be smoothed is placed inside the chamber.

Preferably, the product is placed on a table 140 (FIG. 4) having thetable top located from 1 cm to 5 cm (preferably, 2 cm) above a bottomwall 112 of the chamber. The table 140 is preferably made of glass, butit may be also made of steel, aluminium or other suitable materials.

An evaporator 111 is positioned at the bottom of the chamber, forexample placed within the bottom wall 112. The evaporator 111 may have aform of an indentation, to which a portion of the solvent is transferredthrough a duct 212.

The solvent may be transferred to the evaporator 111 under a force ofgravity (i.e. without using a pump) from a main solvent tank 211 (FIG.2). This eliminates the need to use solvent-resistant pumps and requiresonly a solvent-resistant duct 212 to guide the solvent from the tank 211to the evaporator 111.

The chamber 110 comprises a circulation system 300, for circulatingsolvent vapors. Preferably, the circulation system 300 comprises a fan311 having a nozzle 313 that influences the air within the chamber forcirculating the solvent vapors inside the chamber 110 in a directionfrom the bottom to the top of the chamber 110 (as indicated in FIG. 1b). The shape of the nozzle shall be preferably selected such as to causea spiral-shaped flow of vapors inside the chamber. Such flow results ineven concentration of vapors inside the chamber. The flow of solventvapors allows the details and thin walls of the product to warm upfaster, which reduces the amount of solvent that concentrates on thesedetails and heat walls, thereby reducing their smoothing as compared tolarger portions of the product. The flow of solvent vapors inside thechamber from the bottom towards the top opposes the gravity force andhelps, at least to a small extent, to retain the original shape of theproduct during the solvent vapor smoothing process, when small elements(details) of the product tend to bend downwards under gravity due to themelting action of the solvent and the high temperature.

The fan 311 is driven by a motor 312, which may be coupled by a belttransmission 316 with a driving shaft 314 protruding inside the chamber110 through a sealed block 315. The sealed block 315 has a multistagesealing 317 and two crowns, wherein the first crown 315A allows to fitthe sealed block to the chamber 110 providing air tightness and thesecond crown 315B allows the solvent to circulate towards the inside ofthe chamber 110. Details of the sealed block 315 and the driving shaftare presented in FIG. 6.

The device is controlled by means of a controller operable via a controlpanel 130, which allows the user of the device to adjust parameters ofthe smoothing process. Depending on the parameters introduced by theuser, such as a type of the geometry of the model (e.g. simple,complex), a material of the model, a solvent type and a desiredintensity of the smoothing effect, the controller calculates the processparameters such as a temperature inside the chamber, an amount of thesolvent to use, pressure etc.

FIG. 2 presents the device in an isometric view, without a cover. Thedevice comprises heating elements 220 distributed on an outer surface ofat least one of the walls 112-116 for heating the interior of thechamber 110. For example, the heating elements 220 may be provided onthe outer surface of the bottom wall 112 and on the outer surface of atop wall 114. The device may further comprise heating elements 220distributed on an outer surface of the side walls 113, 115, 116. Asingle element may be attached to a wall or a plurality of elements,e.g. 6 elements, may be arranged over the outer surface of the wall.Moreover, at least one heating element 220 can be located directly underthe evaporator 111, to effect the heating and evaporating of the solventfrom the evaporator 111. The heating elements 220 located on the topwall 114 can be controlled by a first temperature sensor (e.g. athermistor), the heating elements 220 located on the bottom wall 112 canbe controlled by a second temperature sensor and the heating elements220 located under the evaporator 111 can be controlled by a thirdtemperature sensor. This allows for independent operation of each groupof the heating elements 220 in order to control the rate (intensity) ofevaporation of the solvent and the temperature in the chamber 110. Ifthe walls 112-116 of the chamber are made of a good heat conductor (forexample, aluminium), then heat can be efficiently and uniformlydistributed from the heating elements 220 along the whole wall surface.

FIG. 3 presents the device without the cover in a back view. The solventstored in the main solvent tank 211 is gravitationally transferred tothe evaporator 111 when a solvent dosing valve 213 is opened. A sensorfor measuring a level of the solvent within the evaporator 111 may belocated on an outer surface of the main solvent tank 211 to measure theamount of solvent within the evaporator 111. The sensor may beconfigured to start the measurement if the level of the solvent is abovethe minimum value required for a smoothing process to start.Alternatively, a sensor may be configured to provide only theinformation on whether the level of the solvent is above a predeterminedlevel, wherein the amount of solvent may be calculated based on theduration of opening of the valve that doses the solvent. The amount ofthe transferred solvent depends on the process parameters, for examplethe size of the product, the type of the material it is made of, thedesired degree of initial and final smoothness etc. Various solvents canbe used, for example acetone, isopropyl alcohol, methyl ethyl ketone(MEK, 2-butanone). The main solvent tank 211 may be filled up with thesolvent through an opening 214 located at the front of the device.

The circulation system 300 further comprises a refrigerating module 320which decreases the temperature of the solvent vapor in order tocondense the solvent (in particular, after the smoothing process isfinished). The condensed solvent is transferred gravitationally from therefrigerating module 320 to the main solvent tank 211 through a transfertube 325. The refrigerating module 320 comprises an inlet 323 forcollecting the air saturated with solvent vapors from the upper portionof the chamber 110 and transferring it to a cooling section 321 (FIG.5), and an outlet 326 for exhaling the dried air from the coolingsection 321 back to the chamber 110. Inside the cooling section 321there are located air ducts with multiple ribs 327 for condensing thesolvent from the air. The plurality of ribs 327 increases the coolingsurface of the cooling section 321. The refrigerating module 320 maycomprise Peltier modules 322 which decrease the temperature of innersurfaces of the cooling section 321, to achieve a dew point for aparticular concentration of the solvent in the air within the chamber(i.e. a temperature at which the air is saturated by the solvent vapor).A heat sink 324 is connected to the warm side of the Peltier modules inorder to dissipate the heat away from the refrigerating module 320.Preferably, the heat sink 324 is additionally cooled down by means oftwo or more cooling fans attached to an inner side of the cover of thedevice (the fans are not shown in the drawings). The temperature of thewarm side of the refrigerating module 320 is controlled by a temperaturesensor coupled with the heat sink 324, while the temperature of the coldside of the refrigerating module 320 is controlled by a temperaturesensor coupled with the cooling section 321. The cold side of therefrigerating module 320 can be covered with a layer of a closed cellfoam which prevents condensing of water vapor, present in the air, on anouter surface of the refrigerating module 320. The foam provides heatinsulation and eliminates condensed water vapor from influencing thethermal capacity of the cooling section 321.

Therefore, in general, the circulation system 300 circulates solventvapors inside the chamber 110 in a direction from the bottom to a top ofthe chamber 110 and outside the chamber in a direction from the top tothe bottom of the chamber 110 in a closed loop system (wherein thevapors are preferably cooled and condensed to be guided to a mainsolvent tank 211 and then transferred as liquid solvent to theevaporator 111). FIG. 4 presents the device without the cover andwithout the refrigerating system in an isometric view. The devicefurther comprises a pressure module 410 comprising a pressure valve 411for blocking an exchange of pressure between the chamber 110 and anouter environment, a Tee fitting 412 with one end connected to thepressure valve 411, a second end connected to a vent valve 413 and athird end connected to a vacuum pump 414. The vacuum pump 414 is used toproduce the negative pressure in the chamber 110 before the smoothingprocess is started. The value of the negative pressure in the chamber ismeasured by the strain gauge 240 mounted on an outer surface of the sidewall of the chamber 110, for example mounted at an angle of 45° in thecorner on the outer side of a side wall 116. The strain gauge 240measures the deformation of the metal sheet of the side wall of thechamber 110. Use of the strain gauge as a pressure sensor providesfaster response to pressure changes inside the chamber comparing tostandard pressure sensors. It also eliminates the necessity of utilizingpressure sensors resistant to environments with an explosive atmosphere.

All elements of the device which are in contact with the solvent orsolvent vapors shall be made of solvent-resistant materials, to maintainlong lifetime of the device.

FIG. 7 presents a solvent vapor smoothing process. Before starting theprocess, a product is placed inside the chamber 110, the door 120 isclosed and process parameters are determined, based on input dataincluding: a type of geometry of the model (e.g. simple or complex), amaterial of the product, a type of solvent and a desired intensity ofthe smoothing effect etc. The process parameters that are determinedaccordingly include the amount of solvent to use in the process, theamount of the negative pressure to be generated, the heatingtemperatures of the side walls and the evaporator etc. A skilled personwill realize how to calculate the process parameters based on generalsrules of physics, e.g. the higher the desired smoothing effect, thehigher solvent concentration shall be used. The expected dew point andthe evaporation temperature of the solvent can be calculated based onthe negative pressure that is to be initially generated within thechamber and the amount of solvent that is to be introduced.

First, in step 501, the door 120 is secured to prevent opening of thedoor during the process, which could cause toxic vapors to escape fromthe chamber. For example, the door can be secured with anelectromagnetic lock.

Next, in step 502, the vacuum pump 414 is started to generate thenegative pressure in the chamber. Preferably the negative pressure has avalue from 300 to 800 mbar with respect to the ambient pressure (whereinthe pressure of the ambient environment of the device is typically theatmospheric pressure), i.e. it is lower from the ambient pressure by 300to 800 mbar. The negative pressure protects the chamber fromdepressurization (leaking) due to the subsequent increase of pressureduring solvent vaporization which takes place further in the process.Additionally, the generated negative pressure facilitates the heating ofthe chamber walls, in particular the top wall and the bottom wall,without significant heating of the product and therefore facilitatesgenerating a high temperature gradient between the product and solventvapors before starting the vaporization. The heated walls preventcondensation of the solvent vapors on their surface, which woulddecrease the solvent concentration in the chamber. Furthermorecondensing of the solvent vapors on the top wall of the chamber couldresult in solvent dropping on the models, which could jeopardize resultsof the smoothing process.

Next, in step 503, after achieving a desired value of the negativepressure, the heating of the chamber walls and the evaporator 111 isinitiated. At least one wall, preferably at least the top wall 114, isheated to a first temperature, which is higher than the expected dewpoint temperature of the solvent, and preferably lower than the expectedboiling temperature of the solvent. The bottom wall 112 and the sidewalls 113, 115, 116 are preferably heated by the heating elements 220 aswell. The walls 112-116 are heated by means of thermal conduction of thewall material that transfers heat along the walls from the heatingelements. At least a portion of the evaporator 111 is heated to a secondtemperature, which is higher than the expected boiling temperature ofthe solvent.

Next, in step 504, the solvent is introduced into the evaporator 111, sothat it evaporates as a result of the high temperature of the evaporator111. The amount of the introduced solvent, which is proportional to anopening duration of the dosing valve 213, depends on the desiredsmoothing level, for example it may be from 50 to 300 ml for a chamberworking volume equal from 40 to 50 litters.

Next, in step 505, the evaporated solvent is distributed by thecirculation system (from the bottom to the top of the chamber) and bymeans of convection. The power of the circulation system may becontrolled in order to adjust the rotational velocity of the fan whichdirectly influences the speed of flow of the solvent vapors.

Next, in step 506, the outer surface of the product is smoothed due tothe solvent condensing on the surface of the product. The condensationoccurs due to the fact that the temperature of the product outer surfaceis lower than the temperature of solvent vapors. Heating of the wallscauses heating of the air inside the chamber and consequently gradualheating of the surface of the product. When the outer surface of theproduct achieves the temperature equal to the solvent vaporstemperature, the smoothing process is stopped, because the solvent stopscondensing on the product surface. Depending on the desired smoothinglevel, the smoothing step may last from 5 to 20 min. Most of thesmoothed products have a complicated geometry, with regions of greatervolumes and thin-wall elements of a smaller volume which tend to warm upfaster, and therefore the time during which they react with the solventis shorter. Shorter reaction time has a positive effect, because theprolonged solvent condensation of the surface of small elements couldcause the solvent to penetrate inside the structure of the product andcould decrease its strength properties, which eventually would cause itsdeformation. The circulation system may operate periodically orcontinuously (optionally with variable operating power) during thesmoothing step. During the smoothing the heating elements 220 can bestill active to maintain the initial temperatures.

After the smoothing is finished, in step 507, the heating elements 220are activated in order to heat up at least one of the walls to a thirdtemperature which is higher than the first temperature, preferablyhigher than the expected boiling temperature of the solvent, thereby toheat the air and the product inside the chamber. This allows to quicklyevaporate the reacted solvent from the surface of the product and fromthe surface of the chamber walls. The evaporation of the solvent isenhanced by the negative pressure within the chamber.

Next, in step 508, the solvent vapors flow through the refrigeratingunit. The inner surfaces of the cooling module are cooled below the dewpoint temperature for the particular concentration and pressure of thesolvent. The solvent condenses on the walls of the cooling section andgravitationally flows down to the main solvent tank 211. In step 508 theheating elements can be operated with less than 100% of their maximumpower, for example with 50% of their power. Alternatively, after thesmoothing step 506, the step of heating the chamber 507 and the step ofcooling the solvent vapors 508 may be performed in an opposite order.The steps 507 and 508 or 508 and 507 may be sequentially repeated untilthe desired solvent concentration is achieved. For example, the desiredsolvent concentration for acetone or 2-butanone may be below 40% of thelower flammability limit.

Next, in step 509, the temperature inside the chamber is equalized withthe room temperature. Next, in step 510, after the chamber is cooleddown, the vent valve is opened to equalize the pressure and theelectromagnetic lock is opened. Subsequently the door may be opened andthe smoothed product may be taken out from the chamber.

Due to the fact that solvent vapors act only on the surface of theproduct, then directly after the end of the process the smoothed productretains its primary plastic properties. Additionally the solvent vaporsmoothing process merges the layers of the product, therefore its outerstructure is integrated, and the strength parameters of the product areincreased.

If some of the regions of the smoothed product have to be protectedagainst solvent vapors, it is possible to cover them with a tape whichis resistant to the solvent. For example, a kapton tape, which is easilyadaptable to different shapes of products, may be used to mask theregions which are to remain intact during the smoothing process.

Owing to the presence of the initial negative pressure and solventvapors condensation step (or steps), the presented device and the methodare safe for a user and the environment, because the hazard of anexplosion or a risk for the solvent escaping from the chamber issignificantly limited.

While the invention presented herein has been depicted, described, andhas been defined with reference to particular preferred embodiment(s),such references and examples of implementation in the foregoingspecification do not imply any limitation on the invention. It will beevident that various modifications and changes may be made theretowithout departing from the broader scope of the technical concept. Thepresented preferred embodiments are exemplary only, and are notexhaustive of the scope of the technical concept presented herein.Accordingly, the scope of protection is not limited to the preferredembodiment(s) described in the specification, but is only limited by theclaims that follow.

1. A method for solvent vapor smoothing of a surface of a plasticproduct, the method comprising the steps of: placing the plastic productto be smoothed in a closed chamber comprising heated walls and a heatedevaporator for solvent; determining process parameters, comprising anexpected dew point of the solvent and an expected boiling temperature ofthe solvent; heating at least one wall of the chamber to a firsttemperature and heating the evaporator to a second temperature, whereinthe first temperature is higher than the expected dew point temperatureof the solvent and wherein the second temperature is higher than theexpected boiling temperature of the solvent for a current pressurewithin the chamber; introducing a solvent to the evaporator; allowingthe solvent vapors to condense on the outer surface of the product; andcollecting solvent vapors from the chamber.
 2. The method according toclaim 1, wherein the evaporator for solvent is located at a bottom ofthe chamber; and the method further comprises circulating solvent vaporsinside the chamber in a direction from the bottom to a top of thechamber; and collecting solvent vapors from the upper portion of thechamber.
 3. The method according to claim 1, wherein the chamber hasheated walls and the method further comprises, after allowing thesolvent vapors to condense on the outer surface of the product, heatingat least one wall of the chamber, collecting solvent vapors from thechamber and condensing the collected solvent vapors outside the chamber.4. The method according to claim 1, further comprising, beforeintroducing the solvent to the evaporator, generating within the chambera negative pressure with respect to an ambient pressure.
 5. The methodaccording to claim 4, wherein the negative pressure equals 300 to 800mbar.
 6. A device for solvent vapor smoothing of a surface of a plasticproduct, the device comprising: a closed chamber comprising heated wallsand a heated evaporator for solvent; and a controller configured to,before introducing the solvent to the evaporator: determine processparameters, comprising an expected dew point of the solvent and anexpected boiling temperature of the solvent; and activate heatingelements to heat at least one wall of the chamber to a first temperatureand heat the evaporator to a second temperature, wherein the firsttemperature is higher than the expected dew point temperature of thesolvent and wherein the second temperature is higher than the expectedboiling temperature of the solvent for a current pressure within thechamber.
 7. The device according to claim 6, wherein: the evaporator,for solvent is located at a bottom of the chamber; and the devicefurther comprises a circulation system for circulating solvent vaporsinside the chamber in a direction from the bottom to a top of thechamber and outside the chamber in a direction from the top to thebottom of the chamber in a closed loop system.
 8. The device accordingto claim 6, wherein: the chamber further comprises a refrigeratingmodule for collecting solvent vapors from the chamber; and thecontroller is further configured to, after allowing the solvent vaporsto be condensed on the outer surface of the product: activate theheating elements to heat at least one wall of the chamber; and activatethe refrigerating module to condense the collected solvent vaporsoutside the chamber.
 9. The device according to claim 6, furthercomprising a pressure module with a vacuum pump for producing a negativepressure within the chamber.
 10. The device according to claim 6,wherein the refrigerating module comprises air ducts for guiding thecollected solvent vapors, wherein the air ducts are thermally coupledwith Peltier modules.
 11. The device according to claim 10, wherein thewarm side of the Peltier modules is coupled with a heat sink cooled by acooling fan.
 12. The device according to claim 6, further comprising astrain gauge mounted on an outer surface of a side wall of the chamber.13. The device according to claim 6, further comprising anelectromagnetic lock for securing the door of the chamber during thesmoothing process.
 14. The device according to claim 6, furthercomprising a transfer tube for guiding solvent vapors from an inlet atthe upper portion of the chamber to a main solvent tank under the forceof gravity.
 15. The device according to claim 6, wherein the solvent istransferrable from the main solvent tank to the evaporator under theforce of gravity via a solvent dosing valve.